Реферат: Механические свойства элементов Периодической системы Менделеева

Shear Modulus 82,6 GPa

Nickel (Annealed)

Hardness, Vickers 75

Tensile Strength, Ultimate 45 MPa

Modulus of Elasticity 207 GPa

Poisson's Ratio 0,31

Shear Modulus 76 GPa

Nickel (Typical)

Tensile Strength, Ultimate 317 MPa

Tensile Strength, Yield 59 MPa

Elongation at Break 30%

Shear Modulus 76 GPa

Copper (Annealed)

Hardness, Vickers 50

Tensile Strength, Ultimate 210 MPa

Tensile Strength, Yield 33,3 MPa

Elongation at Break 60%

Modulus of Elasticity 110 GPa

Bulk Modulus 140 GPa

Poisson's Ratio 0,343

Shear Modulus 46 GPa

Copper (Cold-Worked)

Hardness, Brinell 89 Converted from Vickers for 500 kg load/10 mm ball Brinell test

Hardness, Rockwell A 35

Hardness, Rockwell B 51

Hardness, Vickers 100

Bulk Modulus 140 GPa

Poisson's Ratio 0,35

Copper (Cold Drawn)

Hardness, Rockwell B 37

Tensile Strength, Ultimate 344 MPa

Tensile Strength, Yield 333,4 MPa

Elongation at Break 14%

Bulk Modulus 140 GPa