Modulus of Elasticity 560 GPa
Osmium (Cold-Worked)
Hardness, Brinell 580 Converted from Vickers for 3000 kg load/10 mm ball Brinell test
Hardness, Rockwell A 80
Hardness, Rockwell C 57
Hardness, Vickers 670
Osmium (Arc-Melted)
Hardness, Brinell 722 Converted from Vickers for 3000 kg load/10 mm ball Brinell test
Hardness, Knoop 822 Converted from Vickers
Hardness, Rockwell A 83,4 Converted from Vickers
Hardness, Rockwell C 64 Converted from Vickers
Hardness, Vickers 800
Iridium (Annealed)
Hardness, Brinell 352 Converted from Vickers for 3000 kg load/10 mm ball Brinell test
Hardness, Rockwell A 69
Hardness, Rockwell C 37
Hardness, Vickers 370
Tensile Strength, Ultimate 1000 MPa
Modulus of Elasticity 524 GPa
Poisson's Ratio 0,26
Shear Modulus 232 GPa Calculated
Iridium (Cold-Drawn)
Hardness, Brinell 565 Converted from Vickers for 3000 kg load/10 mm ball Brinell test
Hardness, Rockwell A 80
Hardness, Rockwell C 56
Hardness, Vickers 650
Tensile Strength, Ultimate 2000 MPa
Platinum (CP Grade, Annealed)
Hardness, Vickers 40
Tensile Strength, Ultimate 125–165 MPa
Elongation at Break 35% in 50 mm
Modulus of Elasticity 171 GPa static in tension
Poisson's Ratio 0,39
Shear Modulus 62 GPa Calculated value
Platinum (CP Grade, Hard Drawn–50% Cold Worked)