Реферат: Механические свойства элементов Периодической системы Менделеева
Tensile Strength, Ultimate 140 MPa
Tensile Strength, Yield 60 MPa
Elongation at Break 12%
Modulus of Elasticity 74 GPain tension
Bulk Modulus 44,5 GPa
Poisson's Ratio 0,213
Shear Modulus 30,5 GPa
Ytterbium
Hardness, Vickers 17
Tensile Strength, Ultimate 72 MPa
Tensile Strength, Yield 66 MPa
Elongation at Break 43%
Modulus of Elasticity 23,7 GPa in tension
Bulk Modulus 30,5 GPa
Poisson's Ratio 0,207
Shear Modulus 9,9 GPa
Lutetium
Hardness, Vickers 44
Tensile Strength, Ultimate 140 MPa
Tensile Strength, Yield 60 MPa
Elongation at Break 12%
Modulus of Elasticity 68,6 GPa in tension
Bulk Modulus 47,6 GPa
Poisson's Ratio 0,261
Shear Modulus 27,2 GPa
Hafnium (Rod)
Tensile Strength, Ultimate 485 MPa
Tensile Strength, Yield 240 MPa
Elongation at Break 25%
Hafnium (Plate)
Tensile Strength, Ultimate 450 MPa Longitudinal
Tensile Strength, Ultimate 470 MPa Transverse
Tensile Strength, Yield 195 MPa Longitudinal