Реферат: Механические свойства элементов Периодической системы Менделеева

Hardness, Brinell 0,9

Hardness, Vickers Max 10

Tensile Strength, Ultimate 4,5 MPa Annealed

Modulus of Elasticity 12,7 GPa in tension

Compressive Yield Strength 2,14 MPa

Poisson's Ratio 0,4498

Shear Modulus 5 GPa Calculated

Tin

Hardness, Brinell 3,9

Tensile Strength, Ultimate 220 MPa

Modulus of Elasticity 41,4 GPa

Poisson's Ratio 0,33

Shear Modulus 18 GPa Calculated

Antimony

Hardness, Brinell 30–58

Hardness, Vickers 30–60

Tensile Strength, Ultimate 11,4 MPa

Modulus of Elasticity 77,759 GPa

Shear Modulus 19 GPa

Tellurium

Hardness, Brinell 25

Tensile Strength, Ultimate 11 MPa

Modulus of Elasticity 40 GPa

Poisson's Ratio 0,33

Shear Modulus 15,16 GPa

Cesium

Bulk Modulus 1,57 GPa

Barium

Modulus of Elasticity 12,8 GPa

Bulk Modulus 10,2 GPa

Poisson's Ratio 0,28

Shear Modulus 6 GPa Calculated

Lanthanum

Hardness, Vickers 28

Tensile Strength, Ultimate 130 MPa